Series catalyst products

(1) HNMCC-A

  The catalyst is produced by using honeycomb ceramics material as the supporter, special material as the coat and noble metals (Palladium and platinum) as the active component, which possesses the advantages of high catalytic activity, high thermal stability, long life, low pressure drop and high intensity et al. The performance of the catalyst is comparable to that of roughly identical foreign products. The catalyst can be widely applied in the purification and deodorization of organic waste gas, which releases from chemical industry, manufacture of oil paint, enameled wire, metal printing, multicolor printing and leather, pharmaceutical industry and municipal sewage. The catalyst can be especially applied in the treatment of the waste gas from acrylonitrile production device.


HNMCCA-A technical indicators


Project
Indicators
Size(Long×Wide×High) mm

(148.5-151.5)×(148.5-151.5)×(49.5-50.5)

Surface m2/g
15~25
Compressive strength,MPa≥
10
Apparent density g/mL
0.65~0.75
Purification indicators
A non-hydrocarbon content with less than 150 GB16297(mL/m3

HNMCC-A technical conditions

Project
Indicators
Use catalyst temperature ℃ ≤
600
Operating pressure MPa ≤
0.5
Gas Kongsu h-1
15000~25000
Mutilated oxygen content (v/v),% ≥

0.5

   

(2)GMNCC

  The catalyst is produced by adopting advanced nano-technology and using alumina as the supporter and noble metals (Palladium and platinum) as the active component, which possesses the advantages of high catalytic activity, good thermal stability and long life. Trace hydrocarbon can be removed from carbon dioxide in the devices used to produce hydrogen, glycol, coal-gas in the oil refinery industry The amount of hydrocarbon can be reduced to less than 10 mL/m3 due to high catalytic activity and thermal stability of the catalyst.

GMNCC technical indicators

Project
Indicators
Surface ,m2/g 
100~140
Compressive strength,N/cm ≥
50
Reactor density,g/mL
0.65~0.75
Size(Waijing×Long),mm
φ(2.2~3.2)×(5~15)
After the total hydrocarbon content of PAH catalytic delinking,mL/m3
Drive consistent with the overall contentGB10621,<20

GMNCC technical conditions

Project
Indicators
Use catalyst temperature,℃≤
600
Operating pressure,MPa≤
3.0
Gas Kongsu,h-1
3000~6000
Mutilated oxygen content(v/v),%

0.2

 

(3)HNMCC-P

  The catalyst is produced by using honeycomb ceramics material as the supporter, composite material formed by rare earth metals and transition metals as the auxiliary reagent and noble metals (Palladium and platinum) as the active component, which possesses the advantages of high catalytic activity, high thermal stability, long life and high intensity et al. The catalyst can be applied in the purification of the waste gas released from the device used to produce acrylic acid in order to remove trace propylene, propane, carbon monoxide and acrolein.

HNMCC-P technical indicators

Project
Indicators
Size(Long×Wide×High),mm
(148.5-151.5)×(148.5-151.5)×(49.5-50.5)
Surface,m2/g
15~25
Compressive strength ,MPa ≥
10
Apparent density,g/ml
0.65~0.75
Purification indicators

Non-a paraffin, morbidity, esters being content with GB16297, less than 150 (mL/m3)

HNMCC-P technical conditions

Project
Indicators
Use catalyst temperature ,℃ ≤
650
Operating pressure,MPa ≤
0.5
Gas Kongsu ,h-1 
15000~28000
Mutilated oxygen content(v/v),% ≥
2.0
Water vapour content(wt),% ≤
3.0